Table 1 Strengths of UD glass/epoxy with different V f
From: Effect of shallow angles on compressive strength of biaxial and triaxial laminates
V f | X T (MPa) | X C (MPa) | Y T (MPa) | Y C (MPa) | S (MPa) |
|---|---|---|---|---|---|
0 | 68 (Momentive Specialty Chemicals Inc. 2006) | 85 (Momentive Specialty Chemicals Inc. 2006) | 68 (Momentive Specialty Chemicals Inc. 2006) | 85 (Momentive Specialty Chemicals Inc. 2006) | – |
0.5 | 1215 (Rolfes et al. 2008) | – | 39.7 (Rolfes et al. 2008) | 91 (Rolfes et al. 2008) | 51.2 (Rolfes et al. 2008) |
0.515 | – | – | 36.7 (Wichmann 2002) | – | – |
0.6 | 1200 (Owens Corning Composite Materials 2011) | 721a | 32.6 (Rolfes et al. 2008) | 105.9 (Rolfes et al. 2008) | 52.7 (Rolfes et al. 2008) |
0.638 | 1430 (Peters et al. 2009) | 850 (Peters et al. 2009) | – | – | – |
1 | 2430 (Owens Corning Composite Materials 2008) | 1640a | – | – | 62.7 (Owens Corning Composite Materials 2008) |
r | 0.989 | 0.971 | −0.998 | 0.820 | 0.998 |