Table 1 Properties of sintered sample

From: Optimization of wear loss in silicon nitride (Si3N4)–hexagonal boron nitride (hBN) composite using DoE–Taguchi method

Sample

1 (4 % hBN)

2 (8 % hBN)

3 (12 % hBN)

4 (16 % hBN)

5 (0 % hBN)

Density (g/cc)

1.96

1.96

1.93

1.84

2.04

Vickers hardness (MPa)

2775.88

2318.17

1741.07

907.96

7484.51

  1. Testing at Central Glass and Ceramic Research Institute, Kolkata (India)