Table 5 The crystallite size and linear shrinkage of the HA sample at various sintering temperature

From: The usability of ark clam shell (Anadara granosa) as calcium precursor to produce hydroxyapatite nanoparticle via wet chemical precipitate method in various sintering temperature

Temperature (°C)

Crystallite size [D (nm)]

Linear shrinkage (%)

Density (g/cm3)

200

26.58

0

2.76

600

29.54

3.08

2.81

800

37.98

6.15

2.96

1000

53.18

11.53

3.12

1100

66.32

14.84

2.93

1200

66.34

16.69

2.86