From: Electronic specific heats for amorphous and crystallized alloys
Number | Samples | States | γ mJ/(mol K2) | δ mJ/(mol K4) | \(\theta_{\text{D}}\)/K |
---|---|---|---|---|---|
1 | Zr41.2Ti3.8Cu12.5Ni10Be a22.5 | Cast | 3.030 | 0.101 | 268.120 |
CR-805 K | 1.830 | 0.053 | 331.500 | ||
2 | Zr52.5Cu17.9Ni14.6Al10Ti b5 | Cast | 3.440 | 0.150 | 234.890 |
CR-973 K | 3.170 | 0.077 | 293.360 | ||
3 | (Cu50Zr50)90Al7Gd c3 | Cast | 4.900 | 0.210 | 209.820 |
CR-520 K | 4.770 | 0.200 | 213.260 | ||
4 | (Cu50Zr50)96Al d4 | Cast | 3.700 | 0.180 | 220.880 |
CR-490 K | 3.461 | 0.165 | 227.380 | ||
5 | (Cu50Zr50)92Al e8 | Cast | 3.060 | 0.170 | 225.290 |
CR-673 K | 2.970 | 0.100 | 268.880 | ||
6 | (Fe0.5Co0.5)72B20Si4Nb f4 | Cast | 5.366 | 0.037 | 374.540 |
CR-923 K | 4.385 | 0.006 | 686.830 | ||
7 | Cu50Zr g50 | Cast | 4.300 | 0.129 | 246.830 |
CR-765 K | 2.740 | 0.120 | 252.840 |