Table 1 2D peak position and sharpness, I G /I 2D ratio

From: Laser-induced etching of few-layer graphene synthesized by Rapid-Chemical Vapour Deposition on Cu thin films

  Graphene on Cu Graphene on SiO 2
Acquisition Raman Shift FWHM IG/I2D Raman Shift FWHM IG/I2D
  (cm-1) (cm-1)   (cm-1) (cm-1)  
1 2711.4 70.0 0.86 2704.0 40.3 1.01
2 2701.3 60.0 0.60 2702.7 37.7 0.79
3 2699.8 49.2 0.56 2699.0 43.8 0.80
4 2698.2 46.6 0.46 2701.1 38.7 0.61
  1. Comparison of the position and FWHM of 2D peaks of subsequent Raman acquisitions as extracted by a single Lorentzian fit and evolution of the IG/I2D ratio (spectra from Figure7, Figure8). Uncertainties of the order of 0.01 – 0.04% for the 2D peak Raman shifts and of 3 – 6% for 2D peak FHWMs have been estimated. Note: results concerning transferred graphene are affected by a higher uncertainty because of pronounced secondary peaks (possibly due to residual PMMA used for graphene transfer) present in the Raman spectra (see Figure7(b)), making the fit procedure less accurate.
Back to article page